@article{oai:tohoku.repo.nii.ac.jp:00046188,
 author = {MASUMOTO, T. and MADDIN, R.},
 journal = {Science reports of the Research Institutes, Tohoku University. Ser. A, Physics, chemistry and metallurgy},
 month = {},
 note = {application/pdf, The elastic and plastic properties of filaments of non-crystalline Pd 20 a/o Si alloy and the changes that occur on crystallization during and after heating at various temperatures have been examined. The transformation to the crystalline states was examined with X-ray and electron diffraction, electrical resistivity and electron microscopy. The mechanical tests were performed over a temperature range between -195 and 500℃ through a range of strain rates from 10^<-2> to 10^<-4> sec.^<-1> The non-crystalline structure was stable below 275℃ but transformed on heating at 300℃ or above to a face centered cubic structure (a_o=4.00-4.05 A), then to an unknown structure and finally to the stable orthorhombic Pd_3Si. The relatively high strength and brittle behavior of the non-crystalline form changed to lower strength but with more ductility on transforming to the metast-able crystalline states. The temperature dependence of the mechanical properties of both the non-crystalline and crystalline states was measured., 紀要類(bulletin), 41984 bytes},
 pages = {200--200},
 title = {The Mechanical Properties of Palladium 20 a/o Silicon Alloy Quenched from the Liquid State},
 volume = {24},
 year = {1972}
}